N/A	Cu110	360 Brass
Nominal Composition, %	99.90 Cu, 0.04 O	61.5 Cu, 3.0 Pb, 35.5 Zn
Commercial Forms	F, R, W, T, P, S	F, R, S
TENSILE STRENGTH	N/A	N/A
ksi	32-36	49-68
Mpa	221-455	338-469
YEILD STRENGTH	N/A	N/A
ksi	10 53	18-45
Mpa	69-365	124-310
Elongation in 2 in (50mm), %	55-4	53-18
Machinability Rate, %	20	100
Melting Point	N/A	N/A
us, ˚F (˚C)	1,949 (1,065)	1,630 (885)
Liquidus, ˚F (˚C)	1,981 (1,083)	1,660 (905)
Density, lb/in³	0.321-0.323	0.307
Specific Gravity	8.89-8.94	8.5
Coefficient of Thermal Epansion x 10^-6 77-572˚F (25-300˚C)	9.8 (17.7)	11.4 (20.5)
Electrical Conductivity (annealed) % IACS	101	26
Thermal Conductivity Btu·ft/(h·ft²·˚F) [cal·cm/(s·cm²·˚C)]	226 (0.934)	67 (0.28)