| 316 MATERIAL COMPOSITION | |||||
| MATERIAL | % | ||||
| Carbon | 0.08 | ||||
| Manganese | 2 | ||||
| Silicon | 1 | ||||
| Phosphorous | 0.04 | ||||
| Sulfur | 0.03 | ||||
| Chromium | 16-18 | ||||
| Nickel | 13 | ||||
| Molybdenum | 2.5 | ||||
| 316 MECHANICAL PROPERTIES | |||||
| TENSILE | N/A | YIELD | N/A | HARDNESS | N/A |
| ksi | MPa | ksi | MPa | Brinell | Rockwell |
| 75 | 515 | 30 | 205 | 217 | 95 |
| 304 MATERIAL COMPOSITION | |||||
| MATERIAL | % | ||||
| Carbon | 0.08 | ||||
| Manganese | 2 | ||||
| Silicon | 1 | ||||
| Phosphorous | 0.04 | ||||
| Sulfur | 0.03 | ||||
| Chromium | 18-20 | ||||
| Nickel | 10 | ||||
| 304 MECHANICAL PROPERTIES | |||||
| TENSILE | N/A | YIELD | N/A | HARDNESS | N/A |
| ksi | MPa | ksi | MPa | Brinell | Rockwell |
| 75 | 515 | 30 | 205 | 201 | 92 |
| 430 MATERIAL COMPOSITION | |||||
| MATERIAL | % | ||||
| Carbon | 0.12 | ||||
| Manganese | 1 | ||||
| Silicon | 1 | ||||
| Phosphorous | 0.04 | ||||
| Sulfur | 0.03 | ||||
| Chromium | 16-18 | ||||
| Nickel | N/A | ||||
| 430 MECHANICAL PROPERTIES | |||||
| TENSILE | N/A | YIELD | N/A | HARDNESS | N/A |
| ksi | MPa | ksi | MPa | Brinell | Rockwell |
| 75 | 517 | 50 | 345 | N/A | B85 |